Radially multi-branched polymer and porous film using the same

ABSTRACT

Disclosed is a novel radially multi-branched polymer. The radially multi-branched polymer includes a central molecule to which side-branches are bonded in at least three positions and has an average molecular weight of 500 to 100,000, the side-branch being selected from the group consisting of a polyalkylene oxide, a polyacrylate, a polyester, a polyamide and derivatives thereof. The radially multi-branched polymer is used for manufacturing a low dielectric insulating film to provide a low dielectric insulating film having easily controllable micropores.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a Divisional of co-pending application Ser. No.10/960,040, filed on Oct. 8, 2004, for which priority is claimed under35 U.S.C. § 120, and this application also claims priority under 35U.S.C. § 119 from Application No. 10-2003-0070376 filed in the Republicof Korea on Oct. 9, 2003, the entire contents of which are herebyincorporated by reference.

TECHNICAL FIELD

The present invention relates to a novel radially multi-branched polymerand particularly to a radially multi-branched polymer that includes acentral molecule (A) to which side-branches (B) are bonded in at leastthree positions and has an average molecular weight of between 500 and100,000. More particularly, the present invention relates to a radiallymulti-branched porogen represented by the following formula (I) andhaving a polyalkylene oxide, a polyacrylate, a polyester, a polyamide orderivatives thereof as a side-branch:

ABi (I)

wherein the central molecule (A) is selected from the group consistingof:

wherein X is H or CH₃; the side-branch (B) is —R or

wherein R is selected from the group consisting of the following R₁ toR₄;R₁ is selected from the group consisting of:(OCH₂CH₂)_(n)OZ, (OCH₂CHCH₃)_(n)OZ, (OCHCH₃CH₂)_(n)OZ,(OCH₂CH₂)_(n)(OCH₂CHCH₃)_(m) (OCH₂CH₂)_(k)OZ,(OCH₂CH₂)_(n)(OCHCH₃CH₂)_(m)(OCH₂CH₂)_(k)OZ,(OCH₂CHCH₃)_(n)(OCH₂CH₂)_(m) (OCH₂CHCH₃)_(k)OZ,(OCHCH₃CH₂)_(n)(OCH₂CH₂)_(m)(OCHCH₃CH₂)_(k)OZ,(OCH₂CHCH₃)_(n)(OCH₂CH₂)_(m) (OCHCH₃CH₂)_(k)OZ, and(OCHCH₃CH₂)_(n)(OCH₂CH₂)_(m) (OCH₂CHCH₃)_(k)OZ;

R₂ is OCOC(CH₃)₂(CH₂CQ(CO₂Z))_(n)W;

R₃ is (O(CH₂)_(n)CO)_(m)OZ;R₄ is (NH(CH₂)_(n)CO)_(n)NZ₂;wherein each of n, m and k represents an integer between 0 and 200;Q is selected from the group consisting of H, CH₃, CH₂CH₃, CH₂CH₂OH andCH₂CH₂NH₂;W is selected from Br, I and H;Z is selected from the group consisting of H, methyl, ethyl, propyl,isopropyl, butyl, isobutyl, tert-butyl, pentyl, isopentyl, neopentyl,cyclopentyl, hexyl, cyclohexyl, vinyl (—CH═CH₂), —CCH, propargyl, allyl,benzyl, acetyl (COCH₃), propionyl, isobutryyl, neopetyryl, CH₂CH₂CH₂Si(OMe)₃, CH₂CH₂CH₂Si (OEt)₃, CH₂CH₂CH₂SiMe (OMe)₂, CH₂CH₂CH₂SiMe (OEt)₂,CH₂CH₂CH₂Si (OMe) Me₂, CH₂CH₂CH₂Si (OEt) Me₂, CH₂CH₂OH and CH₂CH₂NH₂;Y is a linking group between a central molecule and a side-branch,wherein Y is selected from the group consisting of 0 and OCH₂; and i isa natural number of 3 or more.

BACKGROUND ART

Recently, there is an increasing interest in polymeric materials havingnano-sized spherical structures, and their applications are extended toelectro-, bio- and functional polymers and other additives.

According to a recent tendency of reduction in a metal line pitchresulting from high-density integration of semiconductor devices,several problems including propagation delay, cross talk, powerdissipation, etc., may occur. To solve such problems, a method ofreducing RC (resistance×capacitance) delay may be considered first ofall. Particularly, used is a method of reducing resistance of a metalline material and reducing conductance between metal lines. For thepurpose of carrying out such a method, copper (Cu) with goodconductivity is generally used as a metal line material. Otherwise,materials with good insulation property are generally used between metallines. Most insulating materials that are currently used are formed ofsilicon oxides having a dielectric constant of 4.0. Therefore, it isdesirable to reduce the dielectric constant to 2.2, preferably to 2.0,or less.

A method for introducing pores into an insulating film has beenresearched so as to obtain a thin insulating film having a dielectricconstant of 2.2 or less. A material used for such pore generation isreferred to as a porogen (or pore generator: pore-generating organicpolymer), which generates pores particularly by calcination. Linearpolymeric polycaprolactone and polyacrylate, branched polyester havingmultiple side-branches, etc., have been used as pore generators.However, they are not suitable for such use and thus there is a need toimprove them.

In the case of branched polymer or dendrimer used for generating pores,it is difficult to control the molecular weight, molecular weightdistribution, microstructure, etc., and thus to generate microporeshaving a uniform size. Additionally, although there is an example thatcrosslinked nanoparticles have been used to form nanopores, it is alsofound to be difficult to form nanoparticles having a uniform size.Moreover, there is a possibility of pyrolysis residues being present.

BRIEF DESCRIPTION OF THE DRAWINGS

The foregoing and other objects, features and advantages of the presentinvention will become more apparent from the following detaileddescription when taken in conjunction with the accompanying drawings inwhich:

FIG. 1 is a TEM (Transmission Electron Microscope) photograph showing aporous film obtained by using the radially hexa-branched porogenaccording to Example 2 in the amount of 30 wt %; and

FIG. 2 is a photograph taken by an optical microscope showing a porousfilm obtained by using the tetra-branched porogen according toComparative Example 3.

DISCLOSURE OF THE INVENTION

Therefore, the present invention has been made in view of theabove-mentioned problems. It is an object of the present invention toprovide a novel radially multi-branched polymer that is prepared withease, and has a narrow molecular weight distribution and an easilycontrollable fine nano-structure. It is another object of the presentinvention to provide an insulating film obtained by using theabove-described radially multi-branched polymer.

Although conventional pore generators have a linear or bar-shapedstructure, the present inventors intended to provide a pore generatorhaving a spherical structure if possible, so as to inhibit phaseseparation, to generate pores having a small size and uniformdistribution and to improve the strength and/or dielectric constant ofan insulating film.

In order to provide a pore generator having a spherical structure, apore generator consists of a central molecule and side-branches. Abenzyl group is selected as a central molecule, because it shows a highreactivity upon bonding of side-branches and is capable of freerotation, and thus provides a uniform molecular weight distribution andimproved productivity and facilitates mass production. Further,side-branches are bonded to the central molecule as symmetrically aspossible, a pore generation material having a spherical structure isprovided and one example is a radially multi-branched polymerrepresented by the following formula (I).

According to an aspect of the present invention, there is provided aradially multi-branched polymer having a central molecule (A) to whichside-branches (B) are bonded in at least three positions, wherein theradially multi-branched polymer is represented by the following formula(I) and has a polyalkylene oxide, a polyacrylate, a polyester, apolyamide or a derivatives thereof as a side-branch. According toanother aspect of the present invention, there is also provided a lowdielectric insulating film obtained by using the radially multi-branchedpolymer as a porogen:

ABi (I)

wherein the central molecule (A) is selected from the group consistingof:

wherein X is H or CH₃; the side-branch (B) is —R or

wherein R is selected from the group consisting of the following R₁ toR₄;R₁ is selected from the group consisting of:(OCH₂CH₂)_(n)OZ, (OCH₂CHCH₃)_(n)OZ, (OCHCH₃CH₂)_(n)OZ,(OCH₂CH₂)_(n)(OCH₂CHCH₃)_(m) (OCH₂CH₂)_(k)OZ,(OCH₂CH₂)_(n)(OCHCH₃CH₂)_(m) (OCH₂CH₂)_(k)OZ,(OCH₂CHCH₃)_(n)(OCH₂CH₂)_(m)(OCH₂CHCH₃)_(k)OZ,(OCHCH₃CH₂)_(n)(OCH₂CH₂)_(m) (OCHCH₃CH₂)_(k)OZ,(OCH₂CHCH₃)_(n)(OCH₂CH₂)_(m) (OCHCH₃CH₂)_(k)OZ and(OCHCH₃CH₂)_(n)(OCH₂CH₂)_(m)(OCH₂CHCH₃)_(k)OZ;

R₂ is OCOC(CH₃)₂(CH₂CQ(CO₂Z))_(n)W;

R₃ is (O(CH₂)_(n)CO)_(m)OZ;R₄ is (NH(CH₂)_(n)CO)_(m)NZ₂;wherein each of n, m and k represents an integer between 0 and 200;Q is selected from the group consisting of H, CH₃, CH₂CH₃, CH₂CH₂OH andCH₂CH₂NH₂;W is selected from Br, I and H;Z is selected from the group consisting of H, methyl, ethyl, propyl,isopropyl, butyl, isobutyl, tert-butyl, pentyl, isopentyl, neopentyl,cyclopentyl, hexyl, cyclohexyl, vinyl (—CH═CH₂), —CCH, propargyl, allyl,benzyl, acetyl (COCH₃), propionyl, isobutyryl, neopetyryl, CH₂CH₂CH₂Si(OMe)₃, CH₂CH₂CH₂Si (OEt)₃, CH₂CH₂CH₂SiMe (OMe)₂, CH₂CH₂CH₂SiMe (OEt)₂,CH₂CH₂CH₂Si (OMe)Me₂, CH₂CH₂CH₂Si (OEt)Me₂, CH₂CH₂OH and CH₂CH₂NH₂;Y is a linking group between a central molecule and a side-branch,wherein Y is selected from the group consisting of O and OCH₂; and i isa natural number of 3 or more.

When an organopolysiloxane and a porogen are dissolved in an organicsolvent to form a solution, it is preferable that both components aremixed well with each other. The most important factor for such mixing isthe interaction between both components. Therefore, suitable heteroatomsas described above have to be used in positions of R₁, R₂, R₃, R₄, Q, W,Z, etc.

The radially multi-branched polymer according to the present inventionhas an average molecular weight of 500 to 100,000, preferably 500 to50,000. When the molecular weight is less than 500, efficient poregeneration cannot be accomplished. On the other hand, when the molecularweight is greater than 100,000, compatibility with a matrix resindecreases and micropores having a very small size is hardly formed.

According to simulation works, when the molecular weight is 10,000 ormore, stereostructural shape of the radially multi-branched polymer ischanged from a sphere into an ellipsoid. Therefore, it is morepreferable that the radially multi-branched polymer has a sphericalstructure and a molecular weight of 500 to 10,000.

Meanwhile, side-branches having a low molecular weight can provide aporogen having a low molecular weight, while side-branches having a highmolecular weight can provide a porogen having a high molecular weight.For example, side-branches having a molecular weight of about 340 canprovide a hexa-branched porogen having a molecular weight of about 3500.For another example, side-branches having a molecular weight of about1,000 can provide a porogen having a molecular weight of about 10,000.It is possible to control molecular weight in this manner for a tri-,tetra- and penta-branched porogens, too. Further, pores with varioussizes may be formed by varying the molecular weight of a porogen. Forexample, a hexa-branched porogen represented by formula (I), and havinga molecular weight of about 3500 may form pores having a size of about 2nm.

Additionally, the radially multi-branched polymer has at least threebranches, preferably at least four branches and more preferably at leastsix branches. It is preferable that the radially multi-branched polymerincludes symmetrically linked side-branches in order to provide aspherical structure. The more the branches are, the more the structureapproaches a sphere. Further, as the number of branches increases, thepolymer branches are limited in movement, thereby inhibiting phaseseparation. Therefore, it is possible to form a microporous insulatingfilm having a small size and uniform distribution. According tocalculation of molecular structures, a hexa-branched polymer is shown tohave a three-dimensional spherical structure.

The radially multi-branched polymer porogen represented by formula (I)according to the present invention may be prepared by any knownsynthetic procedures including a nucleophilic substitution reactionrepresented by the following reaction scheme 1 or 2; a nucleophilicsubstitution reaction, followed by a benzene ring formation reaction inthe presence of a metal catalyst such as CO₂CO₈ (reaction scheme 3); oran esterification reaction represented by the following reaction scheme4 or 5.

Preparation of Radially Multi-Branched Polymers Through the nucleophilicsubstitution reaction as depicted in reaction scheme 1 may beexemplified as follows: hexakisbromomethyl benzene (wherein L=Br) isreacted with a polyalkylene oxide monoalkyl-ether (whereinR═H—(OCH₂CH₂)_(n)—OZ) or -ester in the presence of a base to form aradially hexa-branched polymer (V) that belongs to formula (I).

When trisbromomethyl benzene, tetrakisbromomethyl benzene orpentakisbromomethyl benzene is used instead of hexakisbromomethylbenzene, a radially tri-branched (II), tetra-branched (III) orpenta-branched (IV) polymer that belongs to formula (I) can be formed,respectively.

Preparation of Radially Multi-Branched Polymers Through the nucleophilicsubstitution reaction as depicted in reaction scheme 2 may beexemplified as follows: hexakishydroxymethyl benzene is reacted with aside-branch of a polyalkylene oxide monoalkyl-ether or -ester having amesylate, tosylate or halide in the presence of a base to form aradially hexa-branched polymer (V) that belongs to formula (I).Similarly to reaction scheme 1, when trishydroxymethyl benzene,tetrakishydroxymethyl benzene or pentakishydroxymethyl benzene is usedinstead of hexakishydroxymethyl benzene, a radially tri-branched (II),tetra-branched (III) or penta-branched (IV) polymer that belongs toformula (I) can be formed, respectively.

Preparation of Radially Multi-Branched Polymers Through the benzene ringformation reaction as depicted in reaction scheme 3 may be exemplifiedas follows: 2-butyne-1,4-diethers are reacted with a small amount ofcatalyst such as CO₂CO₈ to form a radially multi-branched polymerrepresented by formula (I).

According to the above reaction schemes 1 to 3, it is possible toprepare a radially multi-branched polyalkylene oxide (R₁) porogen,polyester (R₃) porogen or polyamide (R₄) porogen. Additionally, porogenshaving a side-branch formed of a di-block or tri-block of the radiallymulti-branched polyalkylene oxide porogen, polyester porogen orpolyamide porogen may be prepared through a synthetic route similar tothe above reaction schemes 1 to 3.

A radially multi-branched polyacrylate porogen may be prepared by anucleophilic substitution reaction (reaction scheme 4) or esterificationreaction (reaction scheme 5), followed by the Atom Transfer RadicalPolymerization (ATRP) and reduction.

Preparation of a Radially Multi-Branched Polyacrylate Through thenucleophilic substitution reaction, followed by ATRP and reduction, asdepicted in reaction scheme 4 may be exemplified as follows: a radiallymulti-branched polymer represented by formula (I) may be formed by themethod comprising the steps of: reacting hexakisbromomethyl benzene withbromoisobutyric acid (wherein W═Br) in the presence of a base to formhexakisbromoisobutylcarbonyloxymethyl benzene; forming a radiallyhexa-branched polymer by reacting hexakisbromo-isobutylcarbonyloxymethylbenzene with a methacrylate in the presence of a catalyst such as Cu;and optionally substituting terminal bromine atoms with hydrogen atomsby using a silane and a radical initiator.

When trisbromomethyl benzene, tetrakisbromomethyl benzene orpentakisbromomethyl benzene is used instead of hexakisbromomethylbenzene, a radially tri-branched (II), tetra-branched (III) orpenta-branched (IV) polymer that belongs to formula (I) can be formed,respectively.

In the above reaction scheme 5 for preparing a radially multi-branchedpolyacrylate, an esterification reaction is performed instead of thenucleophilic substitution reaction utilized in reaction scheme 4.Similarly, when trishydroxymethyl benzene, tetrakis-hydroxymethylbenzene or pentakishydroxymethyl benzene is used instead ofhexakishydroxymethyl benzene, a radially tri-branched (II),tetra-branched (III) or penta-branched (IV) polymer that belongs toformula (I) can be formed, respectively.

Additionally, a di-branched polyoxyalkylene oxide side-branch moleculemay be prepared as depicted in the following reaction scheme 6 or 7.Particularly, a substitution reaction of a dihalogen acetone compound iscarried out and then reduction is performed. Otherwise, a substitutionreaction of a dihalogen acetone compound is carried out and then aWittig reaction, dimethylation reaction and reduction are performed.

Preparation of a Di-Branched Polyoxyalkylene Oxide Side-Branch moleculeaccording to reaction scheme 6 may be exemplified as follows:1,3-dichloroketone (wherein L=Cl) is reacted with a polyalkyleneoxide-monoether (wherein R═H—(OCH₂CH₂)_(n)OZ)) or -monoester in thepresence of a base to form a ketone substituted with the polyalkyleneoxide-monoether or -monoester. Then, a secondary alcohol can be obtainedfrom the resultant ketone by using aluminum hydride or boron hydride, asdepicted in reaction scheme 6.

Preparation of a Di-Branched Polyoxyalkylene Oxide Side-Branch moleculeas depicted in reaction scheme 7 may be exemplified as follows:triphenylphosphino-methoxymethane is transformed into an ylide by thereaction with t-butoxide and the ketone obtained from the above reactionscheme 6 is reacted with the ylide via a Wittig reaction route. Then,dimethylation reaction is carried out by using tribromoboron to form analdehyde. Finally, the resultant aldehyde is reduced with boron hydrideto form a primary alcohol, as depicted in reaction scheme 7.

Similarly, a di-branched polyester side-branch molecule or di-branchedpolyamide side-branch molecule may be prepared by a synthetic routesimilar to reaction scheme 6 or 7.

The radially multi-branched polymer according to the present inventionmay be used as a pore generator for reducing the density of aninsulating film.

When a multi-branched organic polymer is used as a pore generator for asemiconductor insulating material, it is preferable that themulti-branched organic molecule contains no additional heteroatomsbesides H, C, N and O. It is more preferable that the multi-branchedorganic molecule is composed of H, C and O because a low amount ofresidue is present after pyrolysis. Additionally, the multi-branchedorganic polymer is suitably pyrolized under inert conditions at atemperature between 200° C. and 400° C. The radially multi-branchedpolymer represented by formula (I) according to the present invention ispyrolized well at the above temperature.

In order to form a porous insulating film, used are a resin capable offorming a matrix and the radially multi-branched polymer according tothe present invention, as a pore generator.

There is no particular limitation in the matrix-forming resin, but it ispreferable that the resin is thermally stable at the pyrolysistemperature of the radially multi-branched polymer and maintainscompatibility during film formation so as to prevent phase separation.Particularly, when it is used for insulating materials ofsemiconductors, highly heat resistant polymer resins that are thermallystable at a temperature of 400° C. or higher, such as polyimide resins,polyarylene ether resins, polyphenylene resins and derivatives thereofand organopolysiloxane resins are preferably used.

A porogen is suitably used in the weight ratio of [matrix-forming resin:porogen] of 100:2 to 50:50 and preferably 100:2 to 60:40 in order toobtain excellent strength of an insulating film.

To form an insulating film, a spin coating method, a dipping method, aroll coating method, etc., may be used. These methods permit forming ofa film with a predetermined thickness. Among these, a spin coatingmethod is particularly preferable for manufacturing an interlayerdielectric film for a multilayer printed circuit board in asemiconductor device.

Generally, a method for manufacturing a porous insulating film by usinga radially multi-branched polymer includes the steps of: coating acomposition containing a highly heat resistant resin and the radiallymulti-branched polymer, drying and curing the coated composition, andperforming pyrolysis of the radially multi-branched polymer to obtain aporous insulating film.

The resultant porous film is useful for an interlayer insulating filmfor electronic devices, a surface protective film for electronicdevices, an interlayer insulating film for multilayer printed circuitboards, a protective film or insulating protective film for liquidcrystal display devices, a low refractive film, a gas barrier film, anda porous film for embedding bio-molecules or catalysts, or the like.

BEST MODE FOR CARRYING OUT THE INVENTION

Reference will now be made in detail to the preferred embodiments

Reference will now be made in detail to the preferred embodiments of thepresent invention. It is to be understood that the following examplesare illustrative only and the present invention is not limited thereto.

EXAMPLES 1-6 Preparation of Radially Multi-Branched Polymer andManufacture of Insulating Film Comprising the Same EXAMPLE 1 Preparationof Radially Hexa-Branched Polyethylene Oxide Porogen Using NucleophilicSubstitution Reaction (Reaction Scheme 1)

228 mg of NaH from which mineral oil is removed was suspended in 50 mlof distilled 1,4-dioxane at room temperature under nitrogen atmosphere.Next, 3.3 g of polyethylene oxide monomethyl ether having an averagemolecular weight of 350 was added thereto and then the mixture wasstirred for about 1 hour to form oxide anion. Further, 1.0 g ofhexakis(bromomethyl)benzene was added thereto and the mixture wasstirred for about 10 hours while heated to 80° C. Then, the mixture wascooled to room temperature, quenched with 10% HCl solution and shakenwith dichloromethane and deionized water to separate an organic phase.Then, the organic phase was passed through a silica gel column toperform purification. The organic solvent was removed in a rotaryevaporator to obtain 3.5 g of a final product as a pale yellow liquid.

According to GPC (Gel Permeation Chromatography) analysis, the producthad a weight average molecular weight of 2670 and a number averagemolecular weight of 2450. According to TGA (Thermo GravimetricAnalysis), the product was shown to be removed well at 200-400° C.

400 MHz ¹H-NMR, CDCl₃, δ(ppm): 3.28 (s, 3H, OCH₃), 3.44-3.72 (OCH₂CH₂O),4.59 (s, 2H, OCH₂Ph)).

EXAMPLE 2 Preparation of Radially Hexa-Branched Polypropylene OxidePorogen Using Nucleophilic Substitution Reaction (i) (Reaction Scheme 1)2-1. Radially Hexa-Branched Polypropylene Oxide Porogen

228 mg of NaH from which mineral oil is removed was suspended in 50 mlof distilled 1,4-dioxane at room temperature under nitrogen atmosphere.Next, 3.2 g of polypropylene oxide monobutyl ether having an averagemolecular weight of 340 was added thereto and then the mixture wasstirred for about 1 hour to form oxide anion. Further, 1.0 g ofhexakis(bromomethyl)benzene was added thereto and the mixture wasstirred for about 10 hours while heated to 80° C. Then, the mixture wascooled to room temperature, quenched with 10% HCl solution and shakenwith ethyl acetate and deionized water to separate an organic phase.Then, the organic phase was passed through a silica gel column toperform purification. The organic solvent was removed in a rotaryevaporator to obtain 3.3 g of a final product as a pale yellow liquid.

According to GPC analysis, the product had a weight average molecularweight of 3480 and a number average molecular weight of 3010. Accordingto TGA, the product was shown to be removed well at 200-400° C.

400 MHz ¹H-NMR, CDCl₃, δ(ppm): 0.91 (t, 3H), 1.11-1.23 (OCHCH₃CH₂O),1.35 (m, 2H), 1.55 (m, 2H), 3.31-3.69 (OCHCH₃CH₂O), 4.55 (br, 1H,OCH₂Ph), 4.75 (br, 1H, OCH₂Ph).

2-2. Manufacture of Insulating Film

Methyl trimethoxysilane and tetramethoxysilane were mixed in an organicsolvent with a mole ratio of 100:60. Next, 0.005 moles of nitric acidper mole of the silane compounds and 2 moles of water per mole ofhydrolysable functional groups were added to perform hydrolyticcondensation reaction, thereby forming an organopolysiloxane. As aporogen, the hexa-branched polypropylene oxide obtained from Example 2-1was used. After spin coating, the coating layer was warmed to 420° C. at10° C./min and left for 1 hour. The resultant insulating film showed adielectric constant of 2.247 and strength of 4.85 GPa.

EXAMPLE 3 Preparation of Radially Hexa-Branched Polypropylene OxidePorogen Using Nucleophilic Substitution Reaction (ii) (Reaction Scheme1)

228 mg of NaH from which mineral oil is removed was suspended in 50 mlof distilled 1,4-dioxane at room temperature under nitrogen atmosphere.Next, 9.4 g of polypropylene oxide monobutyl ether having

230 mg of NaH from which mineral oil is removed was suspended in 50 mlof distilled 1,4-dioxane at room temperature under nitrogen atmosphere.Next, 3.14 g of polypropylene oxide monobutyl ether having an averagemolecular weight of 340 was added thereto and then the mixture wasstirred for about 1 hour to form oxide anion. Further, 1.0 g ofpentakis(bromomethyl)benzene (C₁₁H₁₁Br₅), which was prepared by themethod disclosed in Japanese Laid-Open Patent No. 1995-242722, was addedthereto and the mixture was stirred for about 10 hours while heated to80° C. Then, the mixture was cooled to room temperature, quenched with10% HCl solution and shaken with ethyl acetate and deionized water toseparate an organic phase. Then, the organic phase was passed through asilica gel column to perform purification. The organic solvent wasremoved in a rotary evaporator to obtain 3.2 g of a final product as apale yellow liquid.

According to GPC analysis, the product had a weight average molecularweight of 3120 and a number average molecular weight of 2910. Accordingto TGA, the product was shown to be removed well at 200-400° C.

400 MHz ¹H-NMR, CDCl₃, δ(ppm): 0.93 (t, 3H), 1.13-1.25 (OCHCH₃CH₂O),1.35 (m, 2H), 1.57 (m, 2H), 3.31-3.70 (OCHCH₃CH₂O), 4.55 (br, 1H,OCH₂Ph), 4.75 (br, 1H, OCH₂Ph)), 7.43 (s, 1H).

5-2. Manufacture of Insulating Film

Example 2-2 was repeated to manufacture an insulating film, except thatthe penta-branched polypropylene oxide obtained from Example 5-1 wasused as a porogen instead of the hexa-branched polypropylene oxideobtained from Example 2-1. The resultant insulating film showed adielectric constant of 2.25 and strength of 4.70 GPa.

EXAMPLE 6 Preparation of Radially Tetra-Branched Polypropylene OxidePorogen Using Nucleophilic Substitution Reaction and Determination ofPhysical Properties 6-1. Radially Tetra-Branched Polypropylene OxidePorogen

220 mg of NaH from which mineral oil is removed was suspended in 50 mlof distilled 1,4-dioxane at room temperature under nitrogen atmosphere.Next, 3.04 g of polypropylene oxide monobutyl ether having an averagemolecular weight of 340 was added thereto and then the mixture wasstirred for about 1 hour to form oxide anion. Further, 1.0 g of1,2,4,5-tetrakis(bromomethyl)benzene (C₁₀H₁₀Br₄) was added thereto andthe mixture was stirred for about 10 hours while heated to 80° C. Then,the mixture was cooled to room temperature, quenched with 10% HClsolution and shaken with ethyl acetate and deionized water to separatean organic phase. Then, the organic phase was passed through a silicagel column to perform purification. The organic solvent was removed in arotary evaporator to obtain 3.0 g of a final product as a pale yellowliquid.

According to GPC analysis, the product had a weight average molecularweight of 2450 and a number average molecular weight of 2290. Accordingto TGA, the product was shown to be removed well at 200-400° C.

400 MHz ¹H-NMR, CDCl₃, δ(ppm): 0.90 (t, 3H), 1.10-1.25 (OCHCH₃CH₂O),1.33 (m, 2H), 1.57 (m, 2H), 3.30-3.70 (OCHCH₃CH₂O), 4.57 (br, 1H,OCH₂Ph), 4.77 (br, 1H, OCH₂Ph)), 7.39 (s, 2H).

6-2. Manufacture of Insulating Film

Example 2-2 was repeated to manufacture an insulating film, except thatthe tetra-branched polypropylene oxide obtained from Example 6-1 wasused as a porogen instead of the hexa-branched polypropylene oxideobtained from Example 2-1. The resultant insulating film showed adielectric constant of 2.27 and strength of 4.55 GPa.

EXAMPLE 7 Preparation of Radially Tri-Branched Polypropylene OxidePorogen Using Nucleophilic Substitution Reaction and Determination ofPhysical Properties 7-1. Tri-Branched Polypropylene Oxide Porogen

210 mg of NaH from which mineral oil is removed was suspended in 50 mlof distilled 1,4-dioxane at room temperature under nitrogen atmosphere.Next, 2.86 g of polypropylene oxide monobutyl ether having an averagemolecular weight of 340 was added thereto and then the mixture wasstirred for about 1 hour to form oxide anion. Further, 1.0 molecularweight of 1800 and a number average molecular weight of 1670. Accordingto TGA, the product was shown to be removed well at 200-40° C.

400 MHz ¹HNMR, CDCl₃, δ(ppm): 0.91 (t, 3H), 1.11-1.23 (OCHCH₃CH₂O), 1.35(m, 2H), 1.55 (m, 2H), 3.31-3.69 (OCHCH₃CH₂O), 4.55 (br, 1H, OCH₂Ph),4.75 (br, 1H, OCH₂Ph)), 7.40 (s, 3H).

7-2. Manufacture of Insulating Film

Example 2-2 was repeated to manufacture an insulating film, except thatthe tri-branched polypropylene oxide obtained from Example 7-1 was usedas a porogen instead of the hexa-branched polypropylene oxide obtainedfrom Example 2-1. The resultant insulating film showed a dielectricconstant of 2.28 and strength of 4.40 GPa.

EXAMPLE 8 Preparation of Radially Hexa-Branched Polyacrylate-BasedPorogen Using ATRP (Reaction Scheme 4) and Determination of PhysicalProperties 8-1. Hexa-Branched Polyacrylate-Based Porogen

2 g of hexakis(bromomethyl)benzene was dissolved in 30 ml of DMSO(dimethyl sulfoxide) as a solvent and 3.2 g of bromoisobutyric acid and3.0 g of K₂CO₃ were added thereto. Next, the mixture was heated forabout 40 hours at 10° C. and an organic phase was separated from themixture with 10% aqueous HCl solution and ether. The organic phase wassubjected to column chromatography to separate 3.4 g of a final productas a white solid. (400 MHz ¹H-NMR, CDCl₃, δ(ppm): 1.91 (s, 6H), 5.23 (s,2H).

Then, 1 g of the white solid and 9 g of methyl methacrylate weredissolved in 30 ml of toluene. 130 mg of CuBr and 1 g of2-pyridinecarboxyaldehyde n-butylimine were added thereto and themixture was heated for 20 hours at 90□. Next, the mixture was cooled toroom temperature and the Cu-containing compound was removed with acelite filter. The filtrate was treated with 10% aqueous HCl solutionand ethyl acetate to separate an organic phase. The organic phase wasdistilled under pressure to obtain a product as a light green solid. Theproduct was dissolved in CH₂Cl₂ and purified by column chromatography toobtain about 9 g of a pale yellow solid. 9 g of the pale yellow solidwas dissolved in oxygen-free benzene and 3 g of tris(trimethylsilyl)silane and 200 mg of AIBN (azo-bis-isobutyronitrile) were added thereto.The mixture was reacted for 20 hours at 70° C. and then benzene wasdistilled out under pressure. Further, recrystallization was performedwith ether to obtain about 8.4 g of a final product as a white solid.According to GPC analysis, the polymer product had Mw (weight averagemolecular weight) of 22000 and PDI (polydispersity index) of 1.41.According to TGA, the product was removed well at a temperature ofbetween 350° C. and 400° C.

400 MHz ¹H-NMR, CDCl₃, δ(ppm): 0.85 (s, 3H), 1.02 (s, 3H), 1.64-2.10 (m,2H), 3.58 (s, 3H), 5.20 (s, 2H).

8-2. Manufacture of Insulating Film

Example 2-2 was repeated to manufacture an insulating film, except thatthe hexa-branched polyacrylate porogen obtained from Example 8-1 wasused instead of the hexa-branched polypropylene oxide obtained fromExample 2-1. The resultant insulating film showed a dielectric constantof 2.26 and strength of 4.74 GPa.

COMPARATIVE EXAMPLES 1-3 Manufacture of Insulating Film COMPARATIVEEXAMPLE 1

Example 2-2 was repeated to manufacture an insulating film, except thata linear polypropylene glycol dibutyl ether having a molecular weight of3500 was used as a porogen (pore generator: pore-generating organicpolymer) instead of the hexa-branched polypropylene oxide obtained fromExample 2-1.

COMPARATIVE EXAMPLES 2 AND 3

Example 2-2 was repeated to manufacture insulating films of ComparativeExamples 2 and 3, except that tetra-branched 2,3,5,6-polyethylene oxideethylene (prepared from Example 57 disclosed in Korean PatentApplication No. 2002-80196) and tetra-branched 2,3,5,6-polyethyleneoxide ethylene (prepared from Example 58, ibid.) were used as a porogen(pore generator: pore-forming organic polymer), respectively, instead ofthe hexa-branched polypropylene oxide obtained from Example 2-1 (SeeTable 1).

TABLE 1 Korean Patent Application No. 2002-80196 Porogen R Comp. Ex.2(Example 57)Comp. Ex. 3(Example 58)

—O—(CH₂CH₂O)n—CHn = 16.3, Mn = 350

Experimental Example 1

Evaluation of Insulating Films

In order to determine physical properties of insulating films usingradially multi-branched polymer porogens according to the presentinvention, mechanical strength and dielectric constant of eachinsulating film were measured as follows:

The insulating film manufactured by using hexa-branched polypropyleneoxide according to Example 2 was used and the condition of the curedinsulating film was observed with an optical microscope and an electronmicroscope. Additionally, dielectric characteristics of the film weredetermined by measuring the dielectric constant in the manner of MIS(metal/insulator/semiconductor).

After observing the inside of the film with an electron microscope,pores greater than 5 nm were not found. This indicates that pores with avery small size were generated (See FIG. 1). The following Table 2 showsthe tendency of mechanical strength and dielectric constant of the filmdepending on siloxane composition and porogen content. As can be seenfrom Table 2, dielectric constant significantly decreases in proportionto the content of a radially multi-branched polymer.

TABLE 2 Amount Porogen Silane (mole Content Refractive StrengthDielectric Monomers ratio) (wt %) Index (GPa) Constant MTMS:TMOS 100:600 1.402 13.48 3.280 10 1.364 10.19 2.975 20 1.326 7.07 2.571 30 1.2894.85 2.247 40 1.249 1.86 1.849

EXPERIMENTAL EXAMPLE 2 Evaluation of Insulating Films Comprising LinearPorogen and Radially Multi-Branched Porogens

In order to compare physical properties of an insulating filmsmanufactured by using a linear porogen with those of an insulating filmmanufactured by using a radially multi-branched polymer porogen, thefollowing experiment was performed.

Insulating films manufactured by using the radially multi-branchedpolymer porogens according to Examples 2, 5, 6, 7 and 8 were used.Additionally, insulating films of Comparative Examples 1 to 3manufactured by using a linear porogen and a tetra-branched porogenprepared according to Korean Patent Application No. 2002-80196, ascontrol. The condition of each cured insulating film was observed withan optical microscope and an electron microscope. Further, dielectriccharacteristics of each film were determined by measuring the dielectricconstant in the manner of MIS (metal/insulator/semiconductor).

The cured film of Comparative Example 1 using a linearpolypropyleneglycol dibutyl ether having a molecular weight of 3500 as aporogen showed a slight striation pattern and partial phase separation,and thus a completely transparent film cannot be obtained. Similarly,the cured film using a tetra-branched porogen of Comparative Example 2showed a slight striation pattern and partial phase separation, and thusa completely transparent film cannot be obtained. Additionally, thecured film using a tetra-branched porogen of Comparative Example 3showed a clear striation pattern and complete phase separation (See,FIG. 2). On the other hand, each of the cured films manufactured byusing porogens according to the preferred embodiments of the presentinvention was a transparent film having excellent coatability with nophase separation (See, FIG. 1).

Further, as can be seen from the following Table 3, the cured film ofExample 2 using a sphere-shaped radially hexa-branchedpolypropyleneglycol ether as a porogen has excellent film coatabilityand non-phase separation behavior compared to Comparative Example 1using a linear polypropyleneglycol ether, even though both porogens havea similar molecular weight. Moreover, when insulating films according toExample 2 and Comparative Example 1 are manufactured to have a similardielectric constant, insulating film of Example 2 shows higher strength.Similarly, when insulating films according to Example 6 and ComparativeExample 2 (each using a tetra-branched porogen) are manufactured to havea similar dielectric constant, insulating film of Example 6 shows higherstrength. Meanwhile, the cured film of Comparative Example 3 obtained byusing a tetra-branched porogen showed complete phase separation and thusit was not possible to measure the dielectric constant and strength.

TABLE 3 Dielectric Strength Porogen Constant (GPa) Ex. 2 Radial(hexa-branched) 2.247 4.85 Ex. 5 Radial (penta-branched) 2.25 4.70 Ex. 6Radial (tetra-branched) 2.27 4.55 Ex. 7 Radial (tri-branched) 2.28 4.40Ex. 8 Radial (hexa-branched) 2.26 4.74 Comp. Ex. 1 Linear 2.249 4.18Comp. Ex. 2 Radial (tetra-branched) 2.27 4.21 Comp. Ex. 3 Radial(tetra-branched) — —

INDUSTRIAL APPLICABILITY

As can be seen from the foregoing, radially multi-branched polymersaccording to the present invention are prepared with ease and haveeasily controllable molecular weight and uniform molecular weightdistribution. When they are used in manufacturing porous insulatingfilms as porogens, it is possible to obtain low dielectric insulatingfilms having easily controllable micropores.

While this invention has been described in connection with what ispresently considered to be the most practical and preferred embodiment,it is to be understood that the invention is not limited to thedisclosed embodiment and the drawings. On the contrary, it is intendedto cover various modifications and variations within the spirit andscope of the appended claims.

1. A method for preparing a multi-branched polymer, which comprisescarrying out a nucleophilic substitution reaction according to thefollowing reaction scheme 1:

wherein X is H or CH₃; R is selected from the group consisting of thefollowing R₁ to R₄; R₁ is selected from the group consisting of:(OCH₂CH₂)_(n)OZ, (OCH₂CHCH₃)_(n)OZ, (OCHCH₃CH₂)_(n)OZ,(OCH₂CH₂)_(n)(OCH₂CHCH₃)_(m) (OCH₂CH₂)_(k)OZ,(OCH₂CH₂)_(n)(OCHCH₃CH₂)_(m) (OCH₂CH₂)_(k)OZ,(OCH₂CHCH₃)_(n)(OCH₂CH₂)_(m)(OCH₂CHCH₃)_(k)OZ,(OCHCH₃CH₂)_(n)(OCH₂CH₂)_(m)(OCHCH₃CH₂)_(k)OZ,(OCH₂CHCH₃)_(n)(OCH₂CH₂)_(m)(OCHCH₃CH₂)_(k)OZ and(OCHCH₃CH₂)_(n)(OCH₂CH₂)_(m)(OCH₂CHCH₃)_(k)OZ; R₂ isOCOC(CH₃)₂(CH₂CQ(CO₂Z))_(n)W; R₃ is (O(CH₂)_(n)CO)_(m)OZ; R₄ is(NH(CH₂)_(n)CO)_(m)NZ₂; wherein each of n, m and k represents an integerbetween 0 and 200; Q is selected from the group consisting of H, CH₃,CH₂CH₃, CH₂CH₂OH and CH₂CH₂NH₂; W is selected from Br, I and H; Z isselected from the group consisting of H, methyl, ethyl, propyl,isopropyl, butyl, isobutyl, tert-butyl, pentyl, isopentyl, neopentyl,cyclopentyl, hexyl, cyclohexyl, vinyl (—CH═CH₂), —CCH, propargyl, allyl,benzyl, acetyl (COCH₃), propionyl, isobutyryl, neopetyryl, CH₂CH₂CH₂Si(OMe)₃, CH₂CH₂CH₂Si (OEt)₃, CH₂CH₂CH₂SiMe (OMe)₂, CH₂CH₂CH₂SiMe (OEt)₂,CH₂CH₂CH₂Si (OMe)Me₂, CH₂CH₂CH₂Si (OEt)Me₂, CH₂CH₂OH and CH₂CH₂NH₂; andL is a halogen atom.
 2. A method for preparing a multi-branched polymer,which comprises carrying out a nucleophilic substitution reactionaccording to the following reaction scheme 2:

wherein X is H or CH₃; R is selected from the group consisting of thefollowing R₁ to R₄; R₁ is selected from the group consisting of:(OCH₂CH₂)_(n)OZ, (OCH₂CHCH₃)_(n)OZ, (OCHCH₃CH₂)_(n)OZ,(OCH₂CH₂)_(n)(OCH₂CHCH₃)_(m) (OCH₂CH₂)_(k)OZ,(OCH₂CH₂)_(n)(OCHCH₃CH₂)_(m) (OCH₂CH₂)_(k)OZ,(OCH₂CHCH₃)_(n)(OCH₂CH₂)_(m)(OCH₂CHCH₃)_(k)OZ,(OCHCH₃CH₂)_(n)(OCH₂CH₂)_(m)(OCHCH₃CH₂)_(k)OZ,(OCH₂CHCH₃)_(n)(OCH₂CH₂)_(m) (OCHCH₃CH₂)_(k)OZ and(OCHCH₃CH₂)₂(OCH₂CH₂)_(m) (OCH₂CHCH₃)_(k)OZ; R₂ isOCOC(CH₃)₂(CH₂CQ(CO₂Z))_(n)W; R₃ is (O(CH₂)_(n)CO)_(m)OZ; R₄ is(NH(CH₂)_(n)CO)_(m)NZ₂; wherein each of n, m and k represents an integerbetween 0 and 200; Q is selected from the group consisting of H, CH₃,CH₂CH₃, CH₂CH₂OH and CH₂CH₂NH₂; W is selected from Br, I and H; Z isselected from the group consisting of H, methyl, ethyl, propyl,isopropyl, butyl, isobutyl, tert-butyl, pentyl, isopentyl, neopentyl,cyclopentyl, hexyl, cyclohexyl, vinyl (—CH═CH₂), —CCH, propargyl, allyl,benzyl, acetyl (COCH₃), propionyl, isobutyryl, neopetyryl, CH₂CH₂CH₂Si(OMe)₃, CH₂CH₂CH₂Si (OEt) 3 CH₂CH₂CH₂SiMe (OMe)₂, CH₂CH₂CH₂SiMe (OEt)₂,CH₂CH₂CH₂Si (OMe)Me₂, CH₂CH₂CH₂Si (OEt)Me₂, CH₂CH₂OH and CH₂CH₂NH₂; andL is a halogen atom.
 3. A method for preparing a multi-branched polymer,which comprises carrying out a benzene ring formation reaction accordingto the following reaction scheme 3:

wherein R is selected from the group consisting of the following R₁ toR₄; R₁ is selected from the group consisting of: (OCH₂CH₂)_(n)OZ,(OCH₂CHCH₃)_(n)OZ, (OCHCH₃CH₂)_(n)OZ,(OCH₂CH₂)_(n)(OCH₂CHCH₃)_(m)(OCH₂CH₂)_(k)OZ,(OCH₂CH₂)_(n)(OCHCH₃CH₂)_(m) (OCH₂CH₂)_(k)OZ,(OCH₂CHCH₃)_(n)(OCH₂CH₂)_(m)(OCH₂CHCH₃)_(k)OZ,(OCHCH₃CH₂)_(n)(OCH₂CH₂)_(m)(OCHCH₃CH₂)_(k)OZ,(OCH₂CHCH₃)_(n)(OCH₂CH₂)_(m)(OCHCH₃CH₂)_(k)OZ and(OCHCH₃CH₂)_(n)(OCH₂CH₂)_(m)(OCH₂CHCH₃)_(k)OZ; R₂ is OCOC(CH₃) 2 (CH₂CQ(CO₂Z))_(n)W; R₃ is (O(CH₂)_(n)CO)_(m)OZ; R₄ is (NH(CH₂)_(n)CO)_(m)NZ₂;wherein each of n, m and k represents an integer between 0 and 200; Q isselected from the group consisting of H, CH₃, CH₂CH₃, CH₂CH₂OH andCH₂CH₂NH₂; W is selected from Br, I and H; Z is selected from the groupconsisting of H, methyl, ethyl, propyl, isopropyl, butyl, isobutyl,tert-butyl, pentyl, isopentyl, neopentyl, cyclopentyl, hexyl,cyclohexyl, vinyl (—CH═CH₂), —CCH, propargyl, allyl, benzyl, acetyl(COCH₃), propionyl, isobutyryl, neopetyryl, CH₂CH₂CH₂Si (OMe)₃,CH₂CH₂CH₂Si (OEt)₃, CH₂CH₂CH₂SiMe (OMe)₂, CH₂CH₂CH₂SiMe (OEt)₂,CH₂CH₂CH₂Si (OMe) Me₂, CH₂CH₂CH₂Si (OEt) Me₂, CH₂CH₂OH and CH₂CH₂NH₂. 4.A method for preparing a multi-branched polymer, which comprisescarrying out a nucleophilic substitution reaction, ATRP (Atom TransferRadical Polymerization) reaction and reduction according to thefollowing reaction scheme 4:

wherein X is H or CH₃; R is selected from the group consisting of thefollowing R₁ to R₄; R₁ is selected from the group consisting of:(OCH₂CH₂) OZ, (OCH₂CHCH₃)_(n)OZ, (OCHCH₃CH₂)_(k)OZ,(OCH₂CH₂)_(n)(OCH₂CHCH₃)_(m) (OCH₂CH₂)_(k)OZ,(OCH₂CH₂)_(k)(OCHCH₃CH₂)_(m) (OCH₂CH₂)_(k)OZ,(OCH₂CHCH₃)_(n)(OCH₂CH₂)_(m) (OCH₂CHCH₃)_(k)OZ,(OCHCH₃CH₂)_(n)(OCH₂CH₂)_(m)(OCHCH₃CH₂)_(k)OZ,(OCH₂CHCH₃)_(n)(OCH₂CH₂)_(m)(OCHCH₃CH₂)_(k)OZ and(OCHCH₃CH₂)_(n)(OCH₂CH₂)_(m)(OCH₂CHCH₃)_(k)OZ; R₂ isOCOC(CH₃)₂(CH₂CQ(CO₂Z))_(n)W; R₃ is (O(CH₂)_(n)CO)_(m)OZ; R₄ is(NH(CH₂)_(n)CO)_(m)NZ₂; wherein each of n, m and k represents an integerbetween 0 and 200; Q is selected from the group consisting of H, CH₃,CH₂CH₃, CH₂CH₂OH and CH₂CH₂NH₂; W is selected from Br, I and H; Z isselected from the group consisting of H, methyl, ethyl, propyl,isopropyl, butyl, isobutyl, tert-butyl, pentyl, isopentyl, neopentyl,cyclopentyl, hexyl, cyclohexyl, vinyl (—CH═CH₂), —CCH, propargyl, allyl,benzyl, acetyl (COCH₃), propionyl, isobutyryl, neopetyryl, CH₂CH₂CH₂Si(OMe)₃, CH₂CH₂CH₂Si (OEt)₃, CH₂CH₂CH₂SiMe (OMe)₂, CH₂CH₂CH₂SiMe (OEt)₂,CH₂CH₂CH₂Si (OMe)Me₂, CH₂CH₂CH₂Si (OEt)Me₂, CH₂CH₂OH and CH₂CH₂NH₂; andL is a halogen atom.
 5. A method for preparing a multi-branched polymer,which comprises carrying out an esterification reaction, ATRP (AtomTransfer Radical Polymerization) reaction and reduction according to thefollowing reaction scheme 5:

wherein X is H or CH₃; R is selected from the group consisting of thefollowing R₁ to R₄; R₁ is selected from the group consisting of:(OCH₂CH₂)_(n)OZ, (OCH₂CHCH₃)_(n)OZ, (OCHCH₃CH₂)_(n)OZ(OCH₂CH₂)_(n)(OCH₂CHCH₃)_(m) (OCH₂CH₂)_(k)OZ,(OCH₂CH₂)_(n)(OCHCH₃CH₂)_(m) (OCH₂CH₂)_(k)OZ,(OCH₂CHCH₃)_(n)(OCH₂CH₂)_(m)(OCH₂CHCH₃)_(k)OZ,(OCHCH₃CH₂)_(n)(OCH₂CH₂)_(m)(OCHCH₃CH₂)_(k)OZ,(OCH₂CHCH₃)_(n)(OCH₂CH₂)_(m)(OCHCH₃CH₂)_(k)OZ and(OCHCH₃CH₂)_(n)(OCH₂CH₂)_(m)(OCH₂CHCH₃)_(k)OZ; R₂ isOCOC(CH₃)₂(CH₂CQ(CO₂Z))_(n)W; R₃ is (O(CH₂)_(n)CO)_(m)OZ; R₄ is(NH(CH₂)_(n)CO)_(m)NZ₂; wherein each of n, m and k represents an integerbetween 0 and 200; Q is selected from the group consisting of H, CH₃,CH₂CH₃, CH₂CH₂OH and CH₂CH₂NH₂; W is selected from Br, I and H; Z isselected from the group consisting of H, methyl, ethyl, propyl,isopropyl, butyl, isobutyl, tert-butyl, pentyl, isopentyl, neopentyl,cyclopentyl, hexyl, cyclohexyl, vinyl (—CH═CH₂), —CCH, propargyl, allyl,benzyl, acetyl (COCH₃), propionyl, isobutyl, neopetyryl, CH₂CH₂CH₂Si(OMe)₃, CH₂CH₂CH₂Si (OEt)₃, CH₂CH₂CH₂SiMe (OMe)₂, CH₂CH₂CH₂SiMe(OEt)₂,CH₂CH₂CH₂Si(OMe)Me₂, CH₂CH₂CH₂Si(OEt)Me₂, CH₂CH₂OH and CH₂CH₂NH₂; and Lis a halogen atom.
 6. The method for preparing a multi-branched polymeraccording to claim 1, wherein

is used instead of H—R in reaction scheme 1, wherein X is H or CH₃; R isselected from the group consisting of the following R₁ to R₄; R₁ isselected from the group consisting of: (OCH₂CH₂)_(n)OZ,(OCH₂CHCH₃)_(n)OZ, (OCHCH₃CH₂)_(n)OZ, (OCH₂CH₂)_(n)(OCH₂CHCH₃)_(m)(OCH₂CH₂)_(k)OZ, (OCH₂CH₂)_(n)(OCHCH₃CH₂)_(m) (OCH₂CH₂)_(k)OZ,(OCH₂CHCH₃)_(n)(OCH₂CH₂)_(m)(OCH₂CHCH₃)_(k)OZ,(OCHCH₃CH₂)_(n)(OCH₂CH₂)_(m)(OCHCH₃CH₂)_(k)OZ,(OCH₂CHCH₃)_(n)(OCH₂CH₂)_(m)(OCHCH₃CH₂)_(k)OZ and(OCHCH₃CH₂)_(n)(OCH₂CH₂)_(m)(OCH₂CHCH₃)_(k)OZ; R₂ isOCOC(CH₃)₂(CH₂CQ(CO₂Z))_(n)W; R₃ is (O(CH₂)_(n)CO)_(m)OZ; R₄ is(NH(CH₂)_(n)CO)_(m)NZ₂; wherein each of n, m and k represents an integerbetween 0 and 200; Q is selected from the group consisting of H, CH₃,CH₂CH₃, CH₂CH₂OH and CH₂CH₂NH₂; W is selected from Br, I and H; Z isselected from the group consisting of H, methyl, ethyl, propyl,isopropyl, butyl, isobutyl, tert-butyl, pentyl, isopentyl, neopentyl,cyclopentyl, hexyl, cyclohexyl, vinyl (—CH═CH₂), —CCH, propargyl, allyl,benzyl, acetyl (COCH₃), propionyl, isobutyryl, neopetyryl, CH₂CH₂CH₂Si(OMe)₃, CH₂CH₂CH₂Si (OEt)₃, CH₂CH₂CH₂SiMe (OMe)₂, CH₂CH₂CH₂SiMe (OEt)₂,CH₂CH₂CH₂Si (OMe)Me₂, CH₂CH₂CH₂Si (OEt)Me₂ CH₂CH₂OH and CH₂CH₂NH₂; and Lis a halogen atom.